Cautiones:
Processus Laminationis
| Lamination temperatus(℃) | Vacation tempus (min) | Lamination tempus (min) |
| 145 | 5-6 | 10-12 |
Morbi laoreet euismod
| Euismod | Projects | Testis signa | Unitas | RP-J9001 |
| | Crassitudo | GB/T 6672-2001 | mm | 0.4~0.8 |
| Roboris distrahentes (post curationem) |
GB/T 13022-91 | Mpa | ≥8 | |
| Prolongatio in confractus (post curationem) | % | ≥800 | ||
| Tenaces film et vitrum cortices vires |
ASTM D903 | N/cm | ≥70 | |
|
Cortices vires tenaces film ac tergum laminam |
N/cm |
≥40 | ||
|
Scelerisque euismod |
Systema |
ASTM 1204 | MD% | ≤4 |
| TD% | ≤2 | |||
| Crucem-coniunctio gradus | ASTM D2765 | % | ≥75% | |
| Electrical perficientur | Volumetric resistivity | GB 1410-89 | Ω.cm | ≥1.0×1015 |
| | Lux transmissionis (post curationem) (280nm~380nm) |
GB/T 24102008 |
% |
≤30 |
| Lux transmissionis (post curationem) (380nm~1100nm) |
GB/T 2410-2008 |
% |
≥90 | |
| | UV canus flavescere index | GB/T29848 | YI | <2.0 |
| Umor et calor canus index flavescere | GB/T29848 |
YI | <4.0 | |